ELECTRICALLY CONDUCTIVE PRODUCT PORTFOLIO

TWO COMPONENT ELECTRICALLY CONDUCTIVE EPOXY RESIN SYSTEMS

Product
Designation

Highlight
Description

Mix
Ratio
B to A

Mixed Viscosity, CPS

Working Time
at 25ºC
100 Gram

Cure Schedules

Hardness
Shore
A or D

Volume
Resistivity
Ohm * CM

MERECO
CLN-658

Flexible
Adhesive

1:1

Thixotropic

2.5 hours

24 hours at RT25ºC
2 hours at 65ºC

75A

0.005

METADUCT
1201

Conductive Epoxy Setting
Adhesive

100:3

Thixotropic

1.5 - 2.0 hours

24 hours at RT 1.25 hours 100ºC

80D

<0.1

METADUCT
1202

Silver Adhesive and Cement

100:4

Thixotropic

1.5 hours

16 hours at RT
3 hours at 65ºC

80D

0.001

METADUCT
1225 SN736

General Purpose
Adhesive

100:4.5

Thin Paste

1 hour

8 hours at RT

85D

0.015

METADUCT
1225 SN742

General Purpose
Adhesive

100:4.5

100,000

2 hours

8 hours at RT

85D

0.018

ONE COMPONENT ELECTRONICALLY CONDUCTIVE EPOXY RESIN SYSTEMS

METADUCT
1206

Single Component
Adhesive

ONE
PART

Thixotropic

6 months

1 hour at
150ºC

85D

0.05

METADUCT
1216

Single Component
Adhesive

ONE
PART

Thixotropic

6 months

12 minutes at 165ºC

85D

0.015

METADUCT
1216-1

Single Component
Adhesive

ONE
PART

Thixotropic

3 months

6 minutes at 165ºC
2 hours at 65ºC

80D

0.019

METADUCT
1216-2

Single Component
Adhesive

ONE
PART

Thixotropic

3 months

4 minutes at 165ºC

80D

0.0008

METADUCT
1240

Flexible
Single Component

ONE
PART

40,000

3 months

15 min at 150ºC

45A

0.0001

METADUCT
1260

Single Component
Frozen Adhesive

ONE
PART

120,000

16 hours

15 min at 150ºC

80D

0.0001

META SHIELD
1234

EMI/RFI
Shielding

ONE
PART

Copper
Dispersion

6 months

30 minutes at RT

N/A

<1 Ohm * cm